An innovative, high build, ‘cold spray’ applied coating, Intertherm 751CSA is based on titanium modified inorganic copolymer technology. Capable of providing corrosion protection, Intertherm 751CSA is a high performance coating applied using standard application equipment curing effectively at ambient temperatures. Suitable for steel operating at temperatures between -196°C (-321°F) and 650ºC (1202ºF), Intertherm 751CSA does not require additional heat curing prior to being placed in service.

Characteristics

Product Chemistry
Heat Resistant Cold Spray Aluminium
Volume Solids
61%
VOC content (EPA method)
420 g/lt
Colour Options
Aluminium
Maximum Dry film thickness
200 μm
Minimum Dry film thickness
100 μm
Number of components
Multi pack
Dry time (at 15°C)
12 Hours
Low Temperature Cure (at 5°C)
18 Hours